Customerzied Wood Cutting Tungsten Carbide Blank Carbide Strip
Grades of finished hard alloy k10 carbide strip
| Properties and applications of carbide for strips | ||||||||
| Grade | Density |
T.R.S MPa |
Hardness HRA |
Performance & application recommended | ||||
| YM6 | 14.9 | 2150 | 90 |
Good wear resistance, used for hard wood, used for processing original wood, aluminum section bar, brass rod and cast iron. |
||||
| YM6A | 14.9 | 1860 | 92 |
Has wear resistance higher than YG6, used for processing hard wood, original wood, aluminum section bar, brass rod and cast iron. |
||||
| YM8 | 14.7 | 2320 | 89.5 |
Wear and percussion resistance , used for processing hard wood, soft wood, ferrous and non-ferrous. |
||||
| YM2T | 14.5 | 2350 | 92 |
Fine carbide, High wear resistance, high bending strength, high resistance to bonding, high thermal strength. Machining of refractory alloys, stainless steel and high manganese steel, etc. |
||||
| YM25 | 14.5 | 2150 | 92.2 |
Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous,metal and non-metallid materials. |
||||
| Other grades of strips may be offered according to customers' requirement. | ||||||||
Application of finished hard alloy k10 carbide strip
Tungsten carbide strips is used for hard wood, used for processing original wood, aluminum section bar, brass rod and cast iron
| Type | Unit:mm | |||||||
| Type | L | W | T | Type | L | W | T | |
| 140 * W * T | 140 | 6 | 1.5-6.0 | 230 * W * T | 230 | 8 | 2.0-6.0 | |
| 140 * W * T | 8 | 230 * W * T | 10 | |||||
| 140 * W * T | 10 | 230 * W * T | 12 | |||||
| 140 * W * T | 12 | 230 * W * T | 16 | |||||
| 140 * W * T | 14 | 230 * W * T | 18 | |||||
| 140 * W * T | 16 | 230 * W * T | 20 | |||||
| 140 * W * T | 18 | 230 * W * T | 22 | |||||
| 140 * W * T | 20 | 2.0-6.0 | 230 * W * T | 25 | 2.5-6.0 | |||
| 140 * W * T | 22 | 230 * W * T | 28 | |||||
| 140 * W * T | 25 | 230 * W * T | 30 | |||||
| 165 * W * T | 165 | 6 | 1.5-6.0 | 230 * W * T | 32 | |||
| 165 * W * T | 8 | 230 * W * T | 40 | |||||
| 165 * W * T | 10 long carbide strip | 320 * W * T | 320 | 8 | 2.0-6.0 | |||
| 165 * W * T | 12 | 320 * W * T | 10 | |||||
| 165 * W * T | 14 | 320 * W * T | 12 | |||||
| 165 * W * T | 16 | 320 * W * T | 14 | |||||
| 165 * W * T | 18 | 320 * W * T | 16 | |||||
| 165 * W * T | 20 | 2.0-6.0 | 320 * W * T | 18 | ||||
| 165 * W * T | 22 | 320 * W * T | 20 | |||||
| 165 * W * T | 24 | 320 * W * T | 22 | |||||
| 165 * W * T | 25 | 320 * W * T | 24 | |||||
| 165 * W * T | 26 | 320 * W * T | 25 | 2.5-6.0 | ||||
| 165 * W * T | 28 | 320 * W * T | 28 | |||||
| 165 * W * T | 30 | 2.5-6.0 | 320 * W * T | 30 | ||||
| 165 * W * T | 32 | 320 * W * T | 32 | |||||
| 165 * W * T | 35 | 320 * W * T | 35 | |||||
| 165 * W * T | 40 | 320 * W * T | 40 | |||||
| ··· | ··· | ··· | ··· | ··· | ··· | ··· | ··· | |
| Other types of strips may be offered according to customers' requirement. | ||||||||
To ensure the quality and the requirements of the drawings can be met before mass production
1st:, Start to prepare the RTP powder as per customer's requirement with our wet-grinding machine
2nd, Before mass production, do a trial pressing and sintering using mould,
3rd, Check the appearances and the sizes of the samples with micrometer, projectors etc.
Test process of Tungsten Carbide Tool Die Insert for Forging Heading Trimming Stamping Pressing Moulds
1st,Mass production press the raw materials to shape blanks,
Notes: all carbide dies blanks must be passed by semi finished inspection
2nd,Sinter blanks to finish (HIP) and finished products inspection,
Notes:10 sets of vacuum sintering furnace and 2set of HIP in the factory ensure the best quality and production capacity.